85% Alumina Zirconium ball is a perfect existence in the alumina ball team, it meets the requirements of high strength, low abrasion and longer service life with a more prominent price advantage. It is the perfect embodiment of strength and beauty, more durable, making users more comfortable. It satisfies the high-quality raw material grinding work well.
Commodity Name |
85% Alumina Zirconium ball |
Brand |
HJMT |
Product code |
HJB-85 |
Al2O3 (%) |
80.0±1.0 |
ZrO3(%) |
4±0.5 |
Density (g/cm³) |
3.30-3.35 |
Water Absorption (%) |
<0.1 |
Hardness (MOHS) |
9 |
Wear Loss (‰) |
0.12±0.02 |
Firing Furnace |
Tunnel Kiln |
Firing Temperature (℃) |
1400 |
Color |
White |
Size(mm) |
10/15/20/25/30/40/45/50 |
Package |
25kgs/bag with pallet. |
Color white close to 92% alumina balls | Pressed type for good strength | |
Shape regularity | Size available from 10 to 60mm |
Size available from 10 to 60mm |
a. Zirconia synthesizes alumina, the ball is tougher.
b. White color makes it can be used for the glaze material grinding.
c. Hardness is good and can replace the using of 92% balls.
d. Saving cost and can also meet production requirements
Chemical analysis report | Wear loss report | |
1. Can you offer sample of 85% Alumina Zirconium ball?
Yes, we would like to offer sample of 85% Alumina Zirconium ball for lab test, samples are free, please you bear the delivery cost.
2. How long is the production lead time for zirconia synthesizes alumina ball?
Usually 7-10days, can be negotiate if your order is urgent.
3. What's the MOQ for zirconia synthesizes alumina balls?
Moq is 1ton.
http://www.hjmtchina.com/